Heat Shrink Tubing Selection Guide
| MIL Spec | Type | Class | Information | RDSNumber |
|---|---|---|---|---|
| M 23053/1 | Chlorinated Polyolefin (Formerly Modified Neoprene) | 1 2 | -550 C to + 900 C -700C to +1210C | R10 R10 |
| M 23053/2 | Polyvinyl Chloride PVC | 1 2 | Flexible Cross Linked Not Cross Linked | V H105 |
| M 23053/3 | Polyvinyl Chloride PVC | 1 2 | Semi-rigid Cross Linked Not Cross Linked | |
| M 23053/4 | Dual Wall Polyolefin | 1 2 3 | Semi-rigid - Melt Liner Flexible – Glue Lined 2:1 Flexible – Glue Lined 3:1 | W5DL O2B2 W3B2 |
| M 23053/5 | Flexible Polyolefin Over-Expanded | 1 1 2 3 | Flame Retardant - Colors 4:1 Shrink Ratio Not Flame Retardant - Clear Only Highly Flame Retardant – Colors | B2 B2(4XC) A2 B2 |
| M 23053/6 | Semi-rigid Polyolefin | 1 2 | Flame Retardant - Colors Not Flame Retardant - Clear | B8 D |
| M 23053/7 | ‘Mylar’ Polyethylene Terephthalate | 1 2 | Longitudinal Seam Spiral Wound | T/07 |
| M 23053/8 | ‘Kynar’ Polyvinylidene Fluoride | Semi-rigid | K | |
| M 23053/9 | Fluorosilicone | Specification Cancelled | ||
| M 23053/10 | Silicone Rubber | Flexible | T/10 | |
| M 23053/11 | FEP Fluorinated Ethylene Propylene | 1 2 | 1.3 to 1.0 Shrink Ratio 1.67 to 1.0 Shrink Ratio | T/11 T/11 |
| M 23053/12 | TFE [PTFE] PolyTetraFluoroEthylene | 1 2 3 4 5 | Heavy Wall 2:1 Shrink Ratio Standard Wall 2:1 Shrink Ratio Thin Wall 2:1 Shrink Ratio Light Wall 2:1 Shrink Ratio Fractional 4:1 Shrink Ratio | T/12 T/12 T/12 T/12 T/12 |
| M 23053/13 | ‘Viton’ ® Fluoroelastomer | Flexible, High temperature[200oC], solvent resistant. -- Clear -- | FE3 KH200 | |
| M 23053/14 | ‘Tefzel’ ® EFTE | Translucent white/Transparent blue -100oC to 150oC | T/14 | |
| M 23053/15 | Heavy Wall Polyolefin Adhesive Lined | 1 2 | .155” Wall .100” Wall | T/15 T/15 CL2 |
| M 23053/16 | Elastomeric Polyolefin | TDR25 | ||
| M 23053/17 | Flame Retardant Translucent Polyolefin | 1 2 | Standard Wall Thin Wall | |
| M 23053/18 | Modified Fluoropolymer Thin Wall | 1 2 3 | Flexible -550C - +1750C Flexible Black or White Only Extremely Flexible -550C - +1500C (900 Shrink Temperature) | K2 T/18 K3 |